Creep behavior of pack cementation aluminide coatings on Grade 91 ferritic–martensitic alloy

Surface and Coatings Technology, Volume 240, 15 February 2014, Pages 32-39.

B.L. Bates, Y. Zhang, S. Dryepondt, B.A. Pint.

a Department of Mechanical Engineering, Tennessee Technological University, Cookeville, TN 38505-0001, USA.

b Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831-6156, USA.

 

Abstract

The creep behavior of various pack cementation aluminide coatings on Grade 91 ferritic–martensitic steel was investigated at 650 °C in laboratory air. The coatings were fabricated in two temperature regimes, i.e., 650 or 700 °C (low temperature) and 1050 °C (high temperature), and consisted of a range of Al levels and thicknesses. For comparison, uncoated specimens heat-treated at 1050 °C to simulate the high temperature coating cycle also were included in the creep test. All coated specimens showed a reduction in creep resistance, with 16–51% decrease in rupture life compared to the as-received bare substrate alloy. However, the specimens heat-treated at 1050 °C exhibited the lowest creep resistance among all tested samples, with a surprisingly short rupture time of < 25 h, much shorter than the specimen coated at 1050 °C. Factors responsible for the reduction in creep resistance of both coated and heat-treated specimens were discussed.

Go To Journal

 

 

Check Also

Fatigue Crack Growth Behavior of WAAM Steel Plates: Experimental Analysis and Comparative Study - Advances in Engineering

Fatigue Crack Growth Behavior of WAAM Steel Plates: Experimental Analysis and Comparative Study